© 2001 Trans Tech Publications Ltd. All Rights ReservedAgüero, A.García, M. C.Muelas Gamo, RaúlSánchez, A.Pérez, Francisco J.Duday, DavidHierro, M. P.Gómez, Consuelo2025-01-202025-01-202001-01-20Materials Science Forum: 369-372(2001)https://www.scientific.net/MSF.369-372.759http://hdl.handle.net/20.500.12666/993The corrosion behaviour of Al slurry coated AISI 310 stainless steel, with and without diffusion heat treatment, was investigated as a wet seal material for molten carbonate fuel cell (MCFC) at 650°C. The results were compared with IVD Al coated AISI 310. Characterization of the samples before and after exposure to the eutectic 62 mol% Li2CO3-38 mol% K2CO3 mixture at 650°C for 1000 h by SEM-EDS and XRD was carried out. The presence of LiAlO2 on the coated samples was confirmed by XRD. The slurry Al-coated stainless steels performed at least as well as the IVD Al coating.engAi Slurry coatingAlloyFuel Cell (FC)Hot CorrosionMolten Carbonateinfo:eu-repo/semantics/article10.4028/www.scientific.net/MSF.369-372.759info:eu-repo/semantics/restrictedAccess